美泰塑胶生产的无卤PA尼龙材料，采用磷、氮等阻燃体系，不含卤素，不受发达国家出口限制；具有低密度、抗水解性能更好的优点，更易镭雕加工，电性能更好。广泛应用于电子电器配件、接线端子、汽车部件、电器开关、电动工具部件等产品。
Meitai produces halogen-free PA (polyamide) nylon materials using phosphorus and nitrogen-based flame retardant systems. These materials do not contain halogens and are not restricted by export regulations of developed countries. They featurelow density, improved hydrolysis resistance, and enhanced ease of laser engraving, as well as superior electrical properties. They are widely used in electronic and electrical components, terminal blocks, automotive parts, electrical switches, and powertool components.
| PA+30%GF无卤阻燃 PA+30%GF Halogen-free Flame Retardant | |||||
| 测试项目 |
检测方式 |
检测条件 | 单位 | RG6130 | RG6230 |
|
密度 Mass Density |
GB/T 1033.1-2008 |
23℃ |
g/cm3 |
1.43 | 1.42 |
|
缺口冲击强度
Impact Strength
|
GB/T 1843-2008 |
23℃ |
KJ/m2 |
12 | 10 |
|
拉伸强度
Tensile Strength
|
GB/T 1040-2006 |
50mm/min |
Mpa |
130 | 145 |
|
断裂伸长率
Tensile Elongation at Break
|
GB/T 1040-2006 |
50mm/min |
% | 4 | 4 |
|
弯曲强度
Flexural Strength
|
GB/T 9341-2008 |
2mm/min |
Mpa |
200 | 220 |
|
弯曲模量
Flexural Modulus
|
GB/T 9341-2008 |
2mm/min |
Mpa |
8500 | 8800 |
|
阻燃
Flammability
|
UL94 | 1.6mm | - | VO | VO |
|
热变形温度
Heat Distortion Temp.
|
GB/T 1634.1-2004 |
1.8MPa 0.34mm |
℃ |
200 | 230 |
| 灼热丝起燃温度 GWIT | GB/T5169.13-2006 | - | ℃ | 775 | 775 |
| 灼热丝引燃指数 GWFI |
GB/T5169.13-2006 |
- |
℃ |
960 | 960 |
| 漏电起痕指数CTI | IEC 60112 |
|
V | 600 | 600 |
| 备注Note | - | - | - | PA6+30%GF无卤阻燃 |
PA66+30%GF无卤
阻燃
|
机械电力、工业零件、汽车交通、电子电器、电路保护装置等
原料、助剂、色粉都来源于国际或国内头部企业，保证了材料、助剂的优异性和质量稳定性，而且每批次都做入厂检验。
青岛美泰塑胶坚持一种产品，一种配方，按照产品的颜色、性能、使用环境、环保等级等定制产品，避免客户选用通用材料时，因性能溢出带来的成本浪费。
使用均化桶均化、色差仪检测，每两个小时打板一次，结合电脑保存的原始配方数据，保证产品稳定；高于国标、行业标准生产工艺，保证可通过第三方检测。
美泰工程师根据所选材料性能给予开模的建议，主动帮助客户修正工艺参数，提高生产效率；如果试料过程中发现模具有缺陷，出具模具的修改方案。